Alternative TitleFatigue Property and Fracture Behavior of 7020 Aluminum Alloys Welded by Laser-MIG Hybrid Welding
Hu, Yanan; Wu, Shengchuan; Song, Zhe; Fu, Yanan; Yuan, Qingxi; 袁清习
Source Publication中国激光
AbstractThe 7020 aluminum alloy joints welded by laser-metal inert-gas arc (MIG) hybrid welding are obtained. The microstructure, mechanical properties, fatigue performance and fracture mechanism of these hybrid welded joints are investigated by the techniques of electron backscatter diffraction and high resolution synchrotron radiation X-ray micro-tomography. The results show that, under the influence of thermal circulation in welding, the grain morphology, size and chemical constituent in different zones of butt-welded joints after cooling show obvious changes. The static tensile strength, yield strength and welding coefficient of hybrid welded joints are 265.34 MPa, 218.85 MPa and 0.74, respectively. When the fatigue life is 2×106 cycles and the survival is 50%, the fatigue strength of hybrid welded joints is 96.13 MPa, and is about 63.14% of that of the base metal, which shows that the welding process significantly deteriorates the performance against fatigue. It is found that the fatigue cracks initiate from a notch with 103 μm depth at the surface in the fusion zone, and show a typical I mode quarter elliptical crack profile. The pores have little effect on the crack growth rate in the stable extension stage. © 2018, Chinese Lasers Press. All right reserved.
Indexed ByEI
EI Accession Number20183205654428
Citation statistics
Document Type期刊论文
First Author AffilicationInstitute of High Energy
Recommended Citation
GB/T 7714
Hu, Yanan,Wu, Shengchuan,Song, Zhe,等. 激光复合焊接7020铝合金的疲劳性能及损伤行为[J]. 中国激光,2018,45(3):302003.
APA Hu, Yanan,Wu, Shengchuan,Song, Zhe,Fu, Yanan,Yuan, Qingxi,&袁清习.(2018).激光复合焊接7020铝合金的疲劳性能及损伤行为.中国激光,45(3),302003.
MLA Hu, Yanan,et al."激光复合焊接7020铝合金的疲劳性能及损伤行为".中国激光 45.3(2018):302003.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Hu, Yanan]'s Articles
[Wu, Shengchuan]'s Articles
[Song, Zhe]'s Articles
Baidu academic
Similar articles in Baidu academic
[Hu, Yanan]'s Articles
[Wu, Shengchuan]'s Articles
[Song, Zhe]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Hu, Yanan]'s Articles
[Wu, Shengchuan]'s Articles
[Song, Zhe]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.