Microstructural stability of NiO-containing spin valves annealed at room temperature
Zhang AM(张爱梅); Cai HL(蔡宏灵); Zhai ZY(翟章印); Du J(杜军); Wu XS(吴小山); Jia QJ(贾全杰)
2009
发表期刊中国物理C
期号11页码:944-948
摘要Microstructure of NiO-containing Co/Cu/Co spin valves(CCC-SV) annealed at room temperature for nearly four years has been studied by synchrotron radiation X-ray diffraction.With the annealing time expanding, the thickness of each sub-layer remains nearly unchanged while the interface roughness varie...
关键词interface roughness X-ray reflectivity spin valves
项目资助者Supported by Open Project of Lab of Solid State Microstructures of Nanjing University (M06007) ; Doctoral Foundation of Hohai University (2084/40701117) ; Natural Science Foundation of Hohai University (2084/408307)
文献类型期刊论文
条目标识符http://ir.ihep.ac.cn/handle/311005/222763
专题多学科研究中心
粒子天体物理中心
推荐引用方式
GB/T 7714
Zhang AM,Cai HL,Zhai ZY,et al. Microstructural stability of NiO-containing spin valves annealed at room temperature[J]. 中国物理C,2009(11):944-948.
APA 张爱梅,蔡宏灵,翟章印,杜军,吴小山,&贾全杰.(2009).Microstructural stability of NiO-containing spin valves annealed at room temperature.中国物理C(11),944-948.
MLA 张爱梅,et al."Microstructural stability of NiO-containing spin valves annealed at room temperature".中国物理C .11(2009):944-948.
条目包含的文件
文件名称/大小 文献类型 版本类型 开放类型 使用许可
7162.pdf(360KB)期刊论文作者接受稿限制开放CC BY-NC-SA请求全文
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[张爱梅]的文章
[蔡宏灵]的文章
[翟章印]的文章
百度学术
百度学术中相似的文章
[张爱梅]的文章
[蔡宏灵]的文章
[翟章印]的文章
必应学术
必应学术中相似的文章
[张爱梅]的文章
[蔡宏灵]的文章
[翟章印]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。